Scholarly article on topic 'Voltage control of magnetic anisotropy in epitaxial Ru/Co2FeAl/MgO heterostructures'

Voltage control of magnetic anisotropy in epitaxial Ru/Co2FeAl/MgO heterostructures Academic research paper on "Nano-technology"

Share paper
Academic journal
Sci. Rep.
OECD Field of science

Academic research paper on topic "Voltage control of magnetic anisotropy in epitaxial Ru/Co2FeAl/MgO heterostructures"


Received: 03 October 2016 Accepted: 17 February 2017 Published: 23 March 2017

Voltage control of magnetic anisotropy in epitaxial Ru/Co2FeAl/ MgO heterostructures

Zhenchao Wen1,3, Hiroaki Sukegawa1, Takeshi Seki2,3, Takahide Kubota2,3, Koki Takanashi2,3 & Seiji Mitani1,4

Voltage control of magnetic anisotropy (VCMA) in magnetic heterostructures is a key technology for achieving energy-efficiency electronic devices with ultralow power consumption. Here, we report the first demonstration of the VCMA effect in novel epitaxial Ru/Co2FeAl(CFA)/MgO heterostructures with interfacial perpendicular magnetic anisotropy (PMA). Perpendicularly magnetized tunnel junctions with the structure of Ru/CFA/MgO were fabricated and exhibited an effective voltage control on switching fields for the CFA free layer. Large VCMA coefficients of 108 and 139 fJ/Vm for the CFA film were achieved at room temperature and 4 K, respectively. The interfacial stability in the heterostructure was confirmed by repeating measurements. Temperature dependences of both the interfacial PMA and the VCMA effect were also investigated. It is found that the temperature dependences follow power laws of the saturation magnetization with an exponent of ~2, where the latter is definitely weaker than that of conventional Ta/CoFeB/MgO. The significant VCMA effect observed in this work indicates that the Ru/ CFA/MgO heterostructure could be one of the promising candidates for spintronic devices with voltage control.

Achieving a sufficient voltage control of magnetic anisotropy (VCMA) in magnetic heterostructures is of particular importance for realizing energy-efficiency electronic devices with ultralow power consumption, such as voltage-torque magnetoresistive random access memories (MRAMs)1'2 and low power logic LSIs3'4. By using voltage-controlled magnetization switching, the power consumption for manipulating a bit cell is proposed to be ~1 fJ, which is two orders of magnitude lower than ~0.1 pJ in the spin transfer torque (STT) technology5. Since magnetic tunnel junctions (MTJs) are key building blocks for high-performance spintronic devices6, the voltage control of magnetization switching in MTJs has greatly promoted the development of the VCMA technology to practical applications7-18. Recently, a ultralow power consumption of ~6 fJ is achieved in state-of-the-art CoFeB/ MgO MTJs with voltage-controlled magnetization switching14'15. Regarding the origin of the VCMA effect, several physical mechanisms have been proposed, such as the modulation of spin-orbit interactions by charge accumulation and depletion19, Rashba effect20,21, voltage-induced redox reaction22, and electro-migration23. Designing and exploring materials for realizing a large magnitude of VCMA effect are still in the ascendant. To date, well-engineered CoFeB8-15, CoFe7,16, FeB17, Fe18, and FePt24,25 ultrathin layers combining with MgO insulators have been extensively studied; however, the voltage effect on the change of magnetic anisotropy is still not large enough in the material systems and the bit-error rate is also a challenge for mass products26. In addition, a large VCMA effect with changing magnetic anisotropy of ~5000 fJ/Vm was observed in Co/GdOx bilayers by voltage-driven O2- migration22; whereas, the speed of ions migration process is very slow and the endurance and scalability are still under discussion. Therefore, advanced materials are extremely required for further development of voltage-controlled spintronic devices.

Ru/Co2FeAl(CFA)/MgO is a novel magnetic heterostructure exhibiting a large perpendicular magnetic anisotropy (PMA) induced by the CFA/MgO interface27-29. A high out-of-plane tunnel magnetoresistance (TMR) ratio of more than 130% was obtained in fully stacked CFA/MgO MTJs on the 4-fold-symetry Ru buffer at room temperature (RT)29. In addition, it was reported that the CFA alloy film can possess a low intrinsic damping constant30, which is greatly advantageous for decreasing bit-error rate for voltage-controlled spintronic devices26.

1National Institute for Materials Science (NIMS), Tsukuba 305-0047, Japan. institute for Materials Research (IMR),

Tohoku University, Sendai 980-8577, Japan. 3Center for Spintronics Research Network (CSRN), Tohoku University,

Sendai 980-8577, Japan. 4Graduate School of Pure and Applied Sciences, University of Tsukuba, 305-8577, Japan.

Correspondence and requests for materials should be addressed to S.M. (email:

Figure 1. Demonstration of VCMA effect in p-MTJs. (a) Schematic illustration of the whole stack structure for p-MTJs. (b) Full R-H loops of a nanoscaled p-MTJ with applying an electric voltage of 1 mV. (c) Minor R-H loops for the p-MTJ under the voltages of -800, 1, and 800 mV. (d) Magnetic phase diagram for the CFA layer from P (AP) to AP (P) magnetic states dependent on voltage and magnetic field. All the measurements were performed at RT.

Recently, giant VCMA effect as high as 1000 fJ/Vm in the CFA/MgO structure was theoretically proposed by first principles calculations31. However, from an experimental point of view, complicated interface reactions and/or inter-diffusions could occur in practical ultrathin heterostructures, such as boron diffusion in Ta/CoFeB/MgO structures32,33, which is particularly significant for both the interfacial PMA and the VCMA effect. Very recently, the interfacial atomic structures of epitaxial ultrathin CFA/Mg0(001) heterostructures were carefully investigated34. Aluminum atoms from the CFA layer significantly interdiffused into MgO, resulting in an Al-deficient Co-Fe-Al/Mg-Al-O structure near the CFA/MgO interface. The magnetization and PMA, as well as VCMA effect, may have been increased by the atomic replacement. Therefore, experimental examination of the VCMA effect in the Ru/CFA/MgO heterostructures is desired for practical spintronic applications, as well as for promoting theoretical investigations on the origin of the VCMA effect.

In this work, we experimentally demonstrate the VCMA effect in Ru/CFA/MgO MTJs. A large coercivity change induced by voltages was observed for the CFA layer in perpendicularly magnetized MTJs (p-MTJs) with the structure of CFA/MgO/CoFeB/Ta/[TbCo/Co]25 where the CFA was a free layer and the CoFeB/Ta/[TbCo/ Co]25 composited layer acted as a reference layer. Quantitative analysis of the VCMA effect was performed by utilizing a magnetoresistance measurement in Ru/CFA/MgO/CoFeB MTJs with an orthogonally magnetic configuration35. Large VCMA coefficients of 108 and 139 fJ/Vm were achieved for the CFA film in the epitaxial Ru/ CFA/MgO structure at RT and 4 K, respectively. Interfacial stability in the structure was demonstrated by repeating measurements of the VCMA effect. Also, the dependences of both interfacial PMA and the VCMA effect on temperature were investigated. It is found that both of them follow power laws of saturation magnetization.

Figure 1a illustrates the whole stack structure for the designed p-MTJs. The deposition condition for each layer is also indicated and the positive direction of applied voltage is defined as the electric current flows from top to bottom layers. The composite upper layers with the structure of CoFeB/Ta/[TbCo/Co]25 are as a reference layer since the TbCo alloy was reported to have a large coercivity36, while the 1-nm-thick CFA is a free layer. The utilization of CoFeB/Ta bilayers in the reference layer is to maintain a high TMR ratio by coherent tunneling through the MgO barrier. The tunneling resistance (R) as a function of out-of-plane magnetic field (H) for a patterned p-MTJ with 100-nm-nanoscale in diameter is shown in Fig. 1b. A direct-current (dc) voltage of 1 mV was applied to measure the resistance here. A TMR ratio of 65% was achieved with a resistance-area product (RA) of ~175 H-^m2. The TMR ratio is defined as 100 x (RAP - RP)/RP, where RAP (RP) is the resistance of the antiparallel,

Figure 2. Quantitative estimation of VCMA effect in the Ru/CFA/MgO heterostructures. (a) Schematic illustration of orthogonally magnetized MTJs with the structure of Ru/CFA/MgO/CoFeB. (b) Normalized TMR curves obtained at different applied voltages under in-plane magnetic field (only the positive field region is shown here). (c) Typical normalized in-plane component of the CFA magnetization. The PMA energy density can be estimated from the shaded area. (d) Electric field dependence of the magnetic anisotropy Kut for the CFA film.

AP (parallel, P) magnetization state. A sharp resistance change observed in the middle of the full R-H loops indicates that a perfect perpendicular magnetization and coherent switching for the CFA free layer were achieved in the heterostructure. Figure 1c shows the minor loops of normalized TMR as a function of magnetic field at the bias voltages of -800 mV, 1 mV, and 800 mV, respectively. A large change in the switching field (Hs) is observed in the CFA layer when the voltages were applied. For instance, the Hs from P to AP state is -780 Oe at 800 mV while it becomes -900 Oe at -800 mV. The AHs of 120 Oe is modulated by the voltages, which is much larger than that in CoFeB/MgO p-MTJs8. The detailed voltage dependence of Hs for the CFA layer from P (AP) to AP (P) magnetization states is shown in Fig. 1d. The coercivities of the CFA layer at each voltage can be derived by (Hs(AP-to-P) - Hs(P-to-AP))/2. It is found that the coercivity decreases with increasing voltage from negative to positive bias direction. In comparison with previously reported ferromagnetic (FM) layer/MgO systems8-18, it is indicated that one of the main mechanisms for the VCMA effect in the p-MTJ is likely to be charge accumulation/ depletion19. The charge accumulation/depletion modulates the electronic occupancy of 3d orbitals in the band structure as well as spin-orbit interactions at the CFA/MgO interface, resulting in the change in effective magnetic anisotropy of the CFA layer. In addition, the maximum current density is calculated to be 4.6 x 105 A/cm2 in the p-MTJ, which indicates STT effect could partially contribute the magnetization switching. The asymmetry of switching fields between positive and negative voltage biases in Fig. 1c and 1d may be attributed to the influence of STT effect.

In order to quantitatively evaluate the VCMA effect in the Ru/CFA/MgO heterostructures, we use a method of in-plane magnetoresistance measurement by utilizing an orthogonally magnetized MTJ35. Figure 2a shows the illustration of the MTJ structure in which the CFA layer is perpendicularly magnetized while the CoFeB layer has in-plane magnetic anisotropy. The external magnetic field was applied along the in-plane direction and R-H loops were measured under different voltages. The VCMA effect was estimated by normalizing the measured curves using the minimum (H = 10 kOe) and maximum (H = 0 Oe) resistances. Figure 2b shows normalized TMR curves at the voltages of10, ± 500, and ± 1100 mV in the positive magnetic field region. A clear dependence of TMR curves on the bias voltages was observed. Since the influence of the bias voltages on the magnitude of TMR ratio is excluded by the normalizing process, the variation in the TMR curves at different voltages indicates a remarkable VCMA effect on the CFA layer. In addition, the maximum current density is estimated to be 1.1 x 102 A/cm2 in the orthogonally magnetized MTJs. The small current density indicates that the influence of STT effect could be negligible in the devices. The PMA of the CFA films was calculated using the measured R-H

Figure 3. Repeating measurements of the VCMA effect. Bias voltages of± 1 V were alternately applied on the MTJs for 300 times. The illustrations indicate the magnetic configuration in the MTJ when a voltage is applied. The inset is the magnification for 50-times measurements.

curves. The conductance of the MTJ is related to the relative angle 6 between the magnetizations of CFA and CoFeB layers, which can be expressed by the equation below,

G(H) = G9O° + (Go° - G9o°)cos 6. (1)

Here G90° (Go°) = 1/.90° (1/.0°) is the conductance of the MTJ in orthogonal (parallel) magnetization configuration. Because the magnetization of CoFeB reference layer is fixed in the film plane, the in-plane component of the magnetization of the CFA layer can be obtained by,

M,„-plm (H) = Ms cos e = M GH) - ^

G0° - G90° (2)

where MS is the saturation magnetization of the CFA film. Furthermore, the PMA energy density Ku can be calculated as,

Ku = Mo Ms f1 HdMn

where is the permeability of free space and Mnorm. is the Min_plane normalized by Ms. A typical normalized in-plane component of the magnetization is shown in Fig. 2c. The shaded area indicates the magnitude of PMA energy density in which the effective value includes demagnetization, bulk and interface contributions to the system. Figure 2d shows the PMA density per unit area, Kut, as a function of applied electric field for the CFA film. At the negative (positive) bias direction, an increase (decrease) in the Kut with increasing the magnitude of electric field was observed. A clear deviation of linear tendency of the Kut-E curve between positive and negative bias directions was shown. The similar behavior was also observed in the CoFeB/MgO8 and Fe/MgO18 heterostruc-tures. Linear fits were performed independently for the positive and negative bias regions. The slope of 108 (50) fJ/ Vm was achieved in the negative (positive) bias direction, which is defined as the coefficient £ of the VCMA effect in the CFA film. The maximum value is much larger than 33 fJ/Vm for the CoFeB film in the Ta/CoFeB/MgO structure10, and comparable to ~100 fJ/Vm for the CoFeB film in the Ir/CoFeB/MgO structure13 and for the FeB film in the MgO/FeB/MgO structure17. Also, we were aware of opposite signs of VCMA effect, i.e., the sign of £, observed between polycrystalline Ru/CoFeB/MgO and Ta/CoFeB/MgO structures10. Interestingly, the sign of the VCMA effect in this work is opposite to that of the polycrystalline Ru/CoFeB/MgO and is the same as that of the Ta/CoFeB/MgO. The sign of the VCMA effect is expected to be sensitive to the electronic structures near the interfaces of a FM layer. Especially, the electronic structures of nonmagnetic (NM) layers adjacent to the FM layer can determine the signs of the VCMA effect, which had been demonstrated by first principles calculations in Pt/ Fe/Pt and Pd/Fe/Pd structures37,38. Therefore, the difference in the ferromagnetic material (CFA and CoFeB) and/ or crystal structure (e.g., polycrystalline hcp Ru and single crystalline Ru(0223) buffer layers) may be responsible for the discrepancy of the signs. However, the buffer layer dependence of the sign of the VCMA effect, as well as the deviation of the VCMA magnitudes between negative and positive bias regions18, are still under discussions.

Furthermore, we investigated the chemical stability of the interfaces in the Ru/CFA/MgO heterostructure by repeatedly measuring the VCMA effect. Figure 3 shows typical VCMA measurements by applying bias voltages of ±1 V back and forth for 300 times. The time interval between two points is one second. The PMA energy density of Kut is calculated at each bias voltage for every time. The inset is a magnified figure for 50-times measurements.

Figure 4. Temperature and magnetic anisotropy dependence of VCMA effect in the Ru/CFA/MgO heterostructures. (a) The dependence of Kut on applied electric field at different temperatures. (b) Temperature dependence of interfacial magnetic anisotropy at zero voltage. (c,d) The VCMA coefficient £ as a function of (c) temperature and (d) magnetic anisotropy for the CFA film in the negative and positive bias regions. The solid lines in (b) and (c) are fitted curves by power laws of Ms(T) with exponents (b) y = 2.00 ± 0.08 and (c) Y = 1.89 ± 0.29, respectively.

The PMA value is well maintained without any decay in the count scale, indicating the crystal structures and interfaces are chemically stable in the Ru/CFA/MgO heterostructure.

Next, we study the temperature dependence of the VCMA effect. Figure 4a shows the applied electric field dependence of Kut at different temperatures. The Kut is calculated by the equation (3) in which the Ms at each temperature was measured as shown in Figure S1 in the Supplementary information. The M—T curve was well fitted by the Bloch's law,

Ms (T ) = Ms (0K)

With decreasing temperature, a clear shift of Kut-E curves is shown, indicating an increase in the magnetic anisotropy for the CFA film at low temperatures. The discrepancy in the linear slopes of the Kut-E curves between positive and negative bias regions was still observed in the entire temperature range. Figure 4b shows the interfacial magnetic anisotropy Kut at zero applied electric field as a function of temperature. The solid line indicates a fitted curve by a power law of Ms(T),

Kut (T ) = Kut (0K)

Ms (T )


It is found that the temperature dependence of Kut is well fitted by the power law with an exponent of Y = 2.00 ± 0.08. The result is corresponding with the theoretical prediction of a Ms2(T) dependence for the magnetic anisotropy especially in the material systems with PMA contributed by high spin-orbit interactions39,40. In general, the temperature dependence of uniaxial anisotropy follows Callen-Callen's Ms3(T) law in a simple ferromagnetic system41. The Ms2(T) power law indicates that the Ru/CFA/MgO system processes a strong spin-orbit interaction where localized moment or two-ion anisotropic exchange makes a main contribution to the temperature dependence of magnetic anisotropy39,40. A similar Ms2(T) dependence was also observed in MgO/CoFeB/

Ta heterostructures with interfacial PMA42. Furthermore, we investigate the VCMA coefficient £ as a function of temperature, as shown in Fig. 4c. The £posi. (£nega.) values are derived by linearly fitting the Kut-E curves in the positive (negative) region. A maximum £ of 139 fJ/Vm is achieved at 4 K for the negative region. Interestingly, the VCMA coefficient £nega. decreases with increasing temperature while the £posi. is nearly independent of the temperature. We fit the temperature dependence of £nega using a power law of Ms(T),

£ (T) = £ (0K)

Ms (T)


The solid line in the Fig. 4c shows a well fitted curve by the power law of Ms(T) with an exponent Y = 1.89 ± 0.29, which is near to the Ms2(T) as the temperature dependence of interfacial magnetic anisotropy. It should be noted that the exponent is definitely smaller than 2.83 in the MgO/CoFeB/Ta system42, which could be attributed to the different spin-orbit coupling behavior in Fe-O hybridization and/or discrepant electronic band structures at the FM/NM interfaces. The effective mechanism for the magnitude of VCMA coefficient is still an open question. The power law fitting could give some insights to the strength of spin-orbit coupling with respect to VCMA. Figure 4d shows the magnetic anisotropy dependence of the VCMA effect. The £nega. obtained in the negative bias region increases with increasing Kut, whereas the £posi. for the positive bias region shows a weak magnetic anisotropy dependence. The asymmetric dependence of VCMA coefficient for positive and negative bias voltage is another important feature in the system. The independence of the £posi. could be related to the origin of the nonlinearity of the VCMA effect. Nonlinear VCMA effects were also reported in several systems in which the possible origins include electronic structures43, Rashba effect21, and strains44. The present temperature dependence in our experiment would provide a significant hint for future studies on the mechanisms of VCMA effects. Theoretical calculations will be strongly required for further understanding of the mechanisms to explain the observed temperature and magnetic anisotropy dependences of the VCMA effect.

In summary, the VCMA effect in the Ru/CFA/MgO heterostructures was experimentally demonstrated. Perpendicularly magnetized MTJs with the structure of CFA/MgO/CoFeB/Ta/[TbCo/Co]25 were fabricated, which exhibited effectively voltage-controlled switching fields for the CFA free layer. Quantitative analysis of the VCMA effect revealed large VCMA coefficients of 108 and 139 fJ/Vm for the CFA film in the epitaxial Ru/ CFA/MgO structure at RT and 4 K, respectively. The chemical stability of the heterostructure was examined by repeating VCMA measurements. It was also found that temperature dependences of both the interfacial PMA and the VCMA effect followed power laws of the saturation magnetization with a material-specific exponent. This study indicates the Ru/CFA/MgO heterostructure could be a promising candidate for spintronic applications with voltage-controlled magnetism.


All the multilayers were deposited by magnetron sputtering in an ultrahigh vacuum system with a base pressure of 3 x 10-7 Pa. The p-MTJ multilayer stack has a structure of MgO(001)-substrate//Ru(40)/CFA(1)/MgO(1.3)/ CoFeB(1.5)/Ta(0.45)/[TbCo(0.3)/Co(0.3)]25/Ta(5)/Ru(10) (unit: nm). The Ru layer was post-annealed at 400 °C for 30 min after deposition in order to form a (0223) epitaxial growth for achieving high-performance CFA/MgO bilayers. The bottom stack of Ru/CFA/MgO/CoFeB/Ta was annealed at 325 °C for 1 h before depositing TbCo/Co multilayers for the purpose of obtaining both high TMR and large PMA simultaneously. The TbCo/Co multilayers were deposited at RT by a co-sputtering method from Co and Tb targets. Furthermore, an orthogonally magnetized MTJ stack with the structure of MgO(001)-substrate//Ru(40)/CFA(1)/MgO(2.2)/CoFeB(20)/Ta(5)/ Ru(10) (unit: nm) was deposited for quantitative analysis of VCMA effect on the CFA layer. The condition of the deposition was identical to that for p-MTJs. The measurement of Ms at low temperatures was performed using a superconducting quantum interference device (SQUID) magnetometer. All the MTJ stacks were patterned into junctions with electric contacts by electron beam lithography and conventional UV lithography combining with Ar ion milling and lift-off technique. The magneto-electrical transport measurements were performed by a dc four-probe method at RT and low temperatures in a physical property measurement system (PPMS).


1. Khalili Amiri, P. et al. Electric-Field-Controlled Magnetoelectric Random Access Memory: Progress, Challenges, and Scaling. IEEE Trans. Magn. 51, 3401507 (2015).

2. Matsukura, F., Tokura, Y. & Ohno, H. Control of magnetism by electric fields. Nat. Nanotechnol. 10, 209-220 (2015).

3. Endoh, T., Koike, H., Ikeda, S., Hanyu, T. & Ohno, H. An Overview of Nonvolatile Emerging Memories-Spintronics for Working Memories. IEEE J. Emerg. Sel. Top. Circuits Syst. 6, 109-119 (2016).

4. Waldrop, M. M. The chips are down for Moore's law. Nat. News 530, 144 (2016).

5. Ohno, H. A window on the future of spintronics. Nat. Mater. 9, 952-954 (2010).

6. Locatelli, N., Cros, V. & Grollier, J. Spin-torque building blocks. Nat. Mater. 13, 11-20 (2014).

7. Shiota, Y. et al. Induction of coherent magnetization switching in a few atomic layers of FeCo using voltage pulses. Nat. Mater. 11, 39-43 (2011).

8. Wang, W.-G., Li, M., Hageman, S. & Chien, C. L. Electric-field-assisted switching in magnetic tunnel junctions. Nat. Mater. 11, 64-68 (2011).

9. Kanai, S. et al. Electric field-induced magnetization reversal in a perpendicular-anisotropy CoFeB-MgO magnetic tunnel junction. Appl. Phys. Lett. 101, 122403 (2012).

10. Shiota, Y. et al. Opposite signs of voltage-induced perpendicular magnetic anisotropy change in CoFeB|MgO junctions with different underlayers. Appl. Phys. Lett. 103, 082410 (2013).

11. Kanai, S. et al. Magnetization switching in a CoFeB/MgO magnetic tunnel junction by combining spin-transfer torque and electric field-effect. Appl. Phys. Lett. 104, 212406 (2014).

12. Liu, H. et al. Manipulation of magnetization switching and tunnel magnetoresistance via temperature and voltage control. Sci. Rep. 5, 18269 (2015).

13. Skowronski, W. et al. Perpendicular magnetic anisotropy of Ir/CoFeB/MgO trilayer system tuned by electric fields. Appl. Phys. Express 8, 053003 (2015).

14. Kanai, S., Matsukura, F. & Ohno, H. Electric-field-induced magnetization switching in CoFeB/MgO magnetic tunnel junctions with high junction resistance. Appl. Phys. Lett. 108, 192406 (2016).

15. Grezes, C. et al. Ultra-low switching energy and scaling in electric-field-controlled nanoscale magnetic tunnel junctions with high resistance-area product. Appl. Phys. Lett. 108, 012403 (2016).

16. Nozaki, T., Shiota, Y., Shiraishi, M., Shinjo, T. & Suzuki, Y. Voltage-induced perpendicular magnetic anisotropy change in magnetic tunnel junctions. Appl. Phys. Lett. 96, 022506 (2010).

17. Nozaki, T. et al. Voltage-Induced Magnetic Anisotropy Changes in an Ultrathin FeB Layer Sandwiched between Two MgO Layers. Appl. Phys. Express 6, 073005 (2013).

18. Nozaki, T. et al. Large Voltage-Induced Changes in the Perpendicular Magnetic Anisotropy of an MgO-Based Tunnel Junction with an Ultrathin Fe Layer. Phys. Rev. Appl. 5, 044006 (2016).

19. Nakamura, K. et al. Giant Modification of the Magnetocrystalline Anisotropy in Transition-Metal Monolayers by an External Electric Field. Phys. Rev. Lett. 102, 187201 (2009).

20. Xu, L. & Zhang, S. Electric field control of interface magnetic anisotropy. J. Appl. Phys. 111, 07C501 (2012).

21. Barnes, S. E., Ieda, J. & Maekawa, S. Rashba Spin-Orbit Anisotropy and the Electric Field Control of Magnetism. Sci. Rep. 4, 4105 (2014).

22. Bauer, U. et al. Magneto-ionic control of interfacial magnetism. Nat. Mater. 14, 174-181 (2014).

23. Rajanikanth, A., Hauet, T., Montaigne, F., Mangin, S. & Andrieu, S. Magnetic anisotropy modified by electric field in V/Fe/ MgO(001)/Fe epitaxial magnetic tunnel junction. Appl. Phys. Lett. 103, 062402 (2013).

24. Weisheit, M. et al. Electric field-induced modification of magnetism in thin-film ferromagnets. Science 315, 349-351 (2007).

25. Seki, T., Kohda, M., Nitta, J. & Takanashi, K. Coercivity change in an FePt thin layer in a Hall device by voltage application. Appl. Phys. Lett. 98, 212505 (2011).

26. Shiota, Y. et al. Evaluation of write error rate for voltage-driven dynamic magnetization switching in magnetic tunnel junctions with perpendicular magnetization. Appl. Phys. Express 9, 013001 (2016).

27. Wen, Z., Sukegawa, H., Mitani, S. & Inomata, K. Perpendicular magnetization of Co2FeAl full-Heusler alloy films induced by MgO interface. Appl. Phys. Lett. 98, 242507 (2011).

28. Li, X. et al. Perpendicular Magnetic Anisotropy of Full-Heusler Films in Pt/Co2FeAl/MgO Trilayers. Appl. Phys. Express 4, 043006 (2011).

29. Wen, Z. et al. A 4-Fold-Symmetry Hexagonal Ruthenium for Magnetic Heterostructures Exhibiting Enhanced Perpendicular Magnetic Anisotropy and Tunnel Magnetoresistance. Adv. Mater. 26, 6483-6490 (2014).

30. Mizukami, S. et al. Low damping constant for Co[sub 2]FeAl Heusler alloy films and its correlation with density of states. J. Appl. Phys. 105, 07D306 (2009).

31. Bai, Z. et al. Magnetocrystalline anisotropy and its electric-field-assisted switching of Heusler-compound-based perpendicular magnetic tunnel junctions. New J. Phys. 16, 103033 (2014).

32. Greer, A. A. et al. Observation of boron diffusion in an annealed Ta/CoFeB/MgO magnetic tunnel junction with standing-wave hard x-ray photoemission. Appl. Phys. Lett. 101, 202402 (2012).

33. Sinha, J. et al. Influence of boron diffusion on the perpendicular magnetic anisotropy in Ta|CoFeB|MgO ultrathin films. J. Appl. Phys. 117, 043913 (2015).

34. Wen, Z. et al. Interdiffusion in epitaxial ultrathin Co2 FeAl/MgO heterostructures with interface-induced perpendicular magnetic anisotropy. Appl. Phys. Express 10, 013003 (2017).

35. Shiota, Y. et al. Quantitative Evaluation of Voltage-Induced Magnetic Anisotropy Change by Magnetoresistance Measurement. Appl. Phys. Express4, 043005 (2011).

36. Ueno, T. et al. Relation between electronic structure and magnetic anisotropy in amorphous TbCo films probed by x-ray magnetic circular dichroism. J. Phys. D: Appl. Phys. 49, 205001 (2016).

37. Tsujikawa, M. & Oda, T. Finite Electric Field Effects in the Large Perpendicular Magnetic Anisotropy Surface Pt/Fe/Pt (001) : A First-Principles Study. Phys. Rev. Lett. 102, 247203 (2009).

38. Haraguchi, S., Tsujikawa, M., Gotou, J. & Oda, T. Electric-field effects on magnetic anisotropy in Pd/Fe/Pd(0 0 1) surface. J. Phys. D: Appl. Phys. 44, 064005 (2011).

39. Staunton, J. B. et al. Temperature Dependent Magnetic Anisotropy in Metallic Magnets from an Ab Initio Electronic Structure Theory: L 1 0 -Ordered FePt. Phys. Rev. Lett. 93, 257204 (2004).

40. Staunton, J. B. et al. Temperature dependence of magnetic anisotropy: An ab initio approach. Phys. Rev. B 74, 144411 (2006).

41. H. B., Callen & E., Callen. The present status of the temperature dependence of magnetocrystalline anisotropy, and the l(l + 1)2 power law. J Phys Chem Solids 27, 1271 (1966).

42. Alzate, J. G. et al. Temperature dependence of the voltage-controlled perpendicular anisotropy in nanoscale MgO|CoFeB|Ta magnetic tunnel junctions. Appl. Phys. Lett. 104, 112410 (2014).

43. Yoshikawa, D., Obata, M., Taguchi, Y., Haraguchi, S. & Oda, T. Possible origin of nonlinear magnetic anisotropy variation in electric field effect in a double interface system. Appl. Phys. Express 7, 113005 (2014).

44. Ong, P. V. et al. Giant voltage modulation of magnetic anisotropy in strained heavy metal/magnet/insulator heterostructures. Phys. Rev. B 92, 020407(R) (2015).


This work was partly supported by the ImPACT program of the Council for Science, Technology and Innovation (Cabinet Office, Government of Japan) and JSPS KAKENHI Grant Number 16H06332. A part of this work was performed under the Inter-university Cooperative Research Program of Institute for Materials Research, Tohoku University (16K0072).

Author Contributions

S.M. and K.T. supervised the study. Z.W. and S.M. designed the experiments. Z.W. and H.S. deposited and micro-fabricated the samples. Z.W., T.S. and T.K. carried out the measurements and analyzed the data. Z.W. and S.M. wrote the manuscript with reviewing by H.S., T.S., T.K. and K.T. All authors discussed the results and the manuscript.

Additional Information

Supplementary information accompanies this paper at Competing Interests: The authors declare no competing financial interests.

How to cite this article: Wen, Z. et al. Voltage control of magnetic anisotropy in epitaxial Ru/Co2FeAl/MgO heterostructures. Sci. Rep. 7, 45026; doi: 10.1038/srep45026 (2017).

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

I/JJN (J) I This work is licensed under a Creative Commons Attribution 4.0 International License. The images Ik^^BS!^* or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

© The Author(s) 2017