0Hindawi Publishing Corporation Journal of Nanomaterials Volume 2013, Article ID 154179, 7 pages http://dx.doi.org/10.1155/2013/154179
Research Article
Nanoindentation and Adhesion Properties of Ta Thin Films
Yuan-Tsung Chen
Department of Materials Science and Engineering, I-Shou University, Kaohsiung 840, Taiwan Correspondence should be addressed to Yuan-Tsung Chen; ytchen@isu.edu.tw Received 1 February 2013; Revised 6 March 2013; Accepted 14 March 2013 Academic Editor: Ugur Serincan
Copyright © 2013 Yuan-Tsung Chen. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Ta films were sputtered onto a glass substrate with thicknesses from 500Ato1500A under the following conditions: (a) as-deposited films were maintained at room temperature (RT), (b) films were postannealed at TA = 150°C for 1 h, and (c) films were postannealed at TA = 250°C for 1h. X-ray diffraction (XRD) results revealed that the Ta films had a body-centered cubic (BCC) structure. Postannealing conditions and thicker Ta films exhibited a stronger Ta (110) crystallization than as-deposited and thinner films. The nanoindention results revealed that Ta thin films are sensitive to mean grain size, including a valuable hardness (H) and Young's modulus (E). High nanomechanical properties of as-deposited and thinner films can be investigated by grain refinement, which is consistent with the Hall-Petch effect. The surface energy of as-deposited Ta films was higher than that in postannealing treatments. The adhesion of as-deposited Ta films was stronger than postannealing treatments because of crystalline degree effect. The maximal H and E and the optimal adhesion of an as-deposited 500-A-thick Ta film were 15.6 GPa, 180 GPa, and 51.56 mJ/mm2, respectively, suggesting that a 500-A-thick Ta thin film can be used in seed and protective layer applications.
1. Introduction
The study of Ta performance is noteworthy because it is a crucial material. Ta is generally inserted as a seed layer, buffer layer, capping layer, and protective layer in a multi-layered structure, which can be used extensively in magnetoresistance random access memory (MRAM) and semiconductor applications [1-5]. It is compatible with the semiconductor process and can also be used as a predeposited layer on substrate or combined with other layers in the epitaxial system, such as Ta/CoCrPt, Ta/Co, and Ta/SiO2/Si systems [6-8]. The superior Ta seed layer needs to have high mechanical properties and strong adhesion, including high hardness (H), Young's modulus (£), and surface energy because Ta seed layer is usually deposited and combined with other layers. Moreover, the performance of Ta-seed multilayered structure is sensitive to a temperate environment. However, few studies have focused on the hardness, Young's modulus, contact angle, surface energy, and adhesion properties of Ta thin films at room temperature (RT) and postannealing temperature conditions. These few studies
only investigated about magnetic and electrical properties of Ta seed multilayered structure [2-4]. In order to justify the contribution of the presented study, the nanomechanical properties and adhesion of Ta thin films in as-deposited and postannealing conditions are worth investigating in detail.
An experiment was conducted to determine the structure, nanomechanical properties, and adhesion of Ta films with X-ray diffraction (XRD), nanoindentation measurement, and contact angle results. The nanoindentation observation yielded considerable information on mechanical properties (hardness and elastic modulus), based on analyses of load-displacement curves [9-12]. The results indicate that the high nanomechanical properties of as-deposited and thinner films can be investigated by grain refinement, which is consistent with the Hall-Petch effect. Surface energy was calculated by contact average angle to understand the adhesion of Ta thin films. The surface energy of as-deposited Ta films was higher than that in postannealing treatments. This indicates that adhesion of as-deposited Ta films was stronger than postannealing treatments because of crystalline degree effect.
- £-(200) (110) BCC-RT ^
1500 A
1000 A -
500 A ~
Ta-BCC-postannealed
fl-(200)(110) (1 t\ 150°C, 1 hr
1500 A
£-(200) j\
1000 A
(110) jAm, A.
5rHw\ 500 A
20 30 40 50 60 70 80 90 20 (deg)
50 60 70 20 (deg)
(110) Ta-BCC-postannealed
_ £-(200) A 250° C, 1 hr
1500 A
£-(200) A
1000 A
£-(200) .
20 30 40 50 60 70 80 90 20 (deg)
Figure 1: XRD results for Ta films at three conditions. (a) Deposited at RT only, (b) postannealing at TA = 150°C for 1 h, and (c) postannealing at TA = 250° C for 1 h.
2. Experimental
Ta thin films were deposited onto a glass substrate by dc magnetron sputtering, with thicknesses (iy) from 500 A to 1500 A, under the following three conditions: (a) substrate temperature (Ts) maintained at RT; (b) Ts = RT, followed by postannealing at TA = 150°C for 1h; (c) postannealing at TA = 250° C for 1h. The postannealing conditions are under inert gas Argon (Ar) atmosphere at chamber pressure 2 x 10-3 Torr. This procedure can solve the oxidation problem of Ta surface [13]. The typical base chamber pressure exceeded 1.5 x 10-7 Torr, and the Ar working chamber pressure was 5 x 10-3 Torr. The structure of the Ta thin film was characterized by using XRD with a CuKa1 line (Philips X'Pert). The average grain size was estimated by full width at half maximum (FWHM, B) and Scherrer's formula. The hardness and Young's modulus of the Ta thin films were measured using an MTS Nanoindenter XP with a Berkovich indenter. Ta thin films can be used intensively in MRAM and/or semiconductor applications. In MRAM applications, thin Ta layers with thicknesses below 100 A are used as adhesion, such
as a seed and/or cap (protection) layer. In the present study, Ta films with thicknesses in the range were investigated. In order to investigate nanomechanical results of Ta thin films at nanoindention measured process, the thicker Ta thickness is suitable than thinner thickness to avoid substrate effect. An indentation load of 1 mN was used to limit the depth of penetration of the indenter to less than 10% of the film thickness. The indentation load was increased in 40 steps, and the penetration depth was measured at each step. Six indentations were investigated in each sample and averaged for more accurate results with a standard deviation. Moreover, the surface energy of the Ta films was calculated from measurement of the contact angle, with water and diiodomethane as test liquids. The surface energy is obtained from the contact angle and some calculations [14-16].
3. Results and Discussion
Figure 1 shows the X-ray diffraction patterns of Ta films under three conditions. Figures 1(a)-1(c) show the X-ray results for the films formed at RT, with postannealing at
1000 Ta thickness (A)
TA= 150° C TA = 250° C
Figure 2: FWHM (B) of (110) peak as a function of thickness of Ta thin films prepared under three conditions.
200 180 160 i? 140
с ■a
и 100 80 60
1000 Ta thickness (A)
TA = 150°C TA = 250°C
Figure 3: Mean grain size as a function of thickness of Ta thin films prepared under three conditions.
TA = 150°C and TA = 250°C. XRD results indicated that the Ta thin films have a body-centered cubic (BCC) structure. This result indicates that Ta films include the substantial crystalline peaks, with a highly crystalline (110) diffraction peak and ^-(200) peak at 1000 A and 1500 A, respectively, under postannealing conditions. However, only main weak (110) peak of Ta 500 A was found at RT and postannealing condition of 150°C. The main (110) peaks with the weak p-(200) peak were found at postannealing conditions of 250°C at 500 A. Figure 1(a) shows that the as-deposited Ta film has a weak crystallization of Ta (110) diffraction peak. Figures 1(b)-1(c) show a multigrain crystalline phenomenon, including (110) and ^-(200) diffraction peaks. In addition, the thicker thickness and postannealing treatment shown in Figures 1(b)-1(c) can induce stronger diffracted intensity than thinner thickness and as-deposited treatment. The diffraction peaks of the Ta thin films became more crystalline as the thickness increased. Crystallization achieved by annealing treatment exceeded that achieved at RT because thermal energy drives grain growth.
The corresponding FWHM (£) of the main Ta (110) peak at three different thicknesses under three conditions is shown in Figure 2. Scherrer's relation was used to estimate mean grain size because the Ta (110) of XRD diffraction result indicated that the intensity of the peak was larger than ^-Ta (200) [17]. Figure 2 shows that weak crystallization occurred under the as-deposited condition and thinner Ta film because it yields a larger FWHM. In contrast, strong crystallization occurred in the postannealing condition and thicker Ta film because of a smaller FWHM. The FWHM for films formed at RT and thin thickness was larger than that of films that have undergone postannealing and thick thickness.
The mean crystalline grain size (D) can be obtained from the measured width of the diffraction peak under crystalline
quality of three conditions, using Scherrer's formula for estimation, as shown in Figure 3. Scherrer's formula is listed [17].
Consider the following:
В cos в'
where к (0.9) is Scherrer's constant, A is the X-ray wavelength of the CuKa1 line, Б is the relative value of the FWHM of the (110) peak, and в is the half angle of the diffraction peak. The formula states that D is proportional to 1/B; thus, a larger Б corresponds to smaller grains. Scherrer's formula yielded mean grain sizes of 63 A, 107 A, and 178 A for 1500-A-thick Ta thin films under the following conditions: (a) with a substrate temperature (Ts) maintained at RT; (b) after postannealing at TA = 150°C for 1 h; (c) after postannealing and heat annealing at TA = 250°C for 1h.
Figure 4(a) shows the hardness (H) of Ta samples under three conditions. Higher values of Ta films were observed in as-deposited and thin Ta films because the grain-refined effect induced the "Hall-Petch" phenomenon. Furthermore, the same result of Young's modulus (E) of Ta films is shown in Figure 4(b). Similarly, the larger values ofTa films occurred in as-deposited and thin Ta films. It also suggests that the "Hall-Petch" equation is suitable for fitting in the Ta layer sufficiently. This indicates that the smaller grains can enhance higher H and E values than larger grains, which also explains a strong nanomechanical performance at as-deposited and thinner films. The result of Ta thin films is consistent with the CoFeB and NiFe thin films [18-20]. The H and E of Ta films declined as the thickness increased, and the postannealing temperature was enhanced. Figure 4 shows that the highest H and E of the Ta films were 15.6 GPa and
TA = 150° C TA = 250° C
1000 Ta thickness (A)
ТА= 150° C ТА = 250° C
1000 Ta thickness (A)
Figure 4: Nano-mechanical properties of Ta samples under three conditions. (a) Hardness and (b) Young's modulus.
180 GPa, respectively, at 500 A of the as-deposited Ta samples, which can be adjusted for seed layer and capping layer applications.
Hardness levels are known to be directly related to grain size, as demonstrated by the Hall-Petch equation [21]:
H = H; + kD
Н{ represents lattice friction stress, к represents the Hall-Petch constant, and D represents the mean grain size.
This formula demonstrates that finer grains are associated with more grain boundaries and induce greater mechanical strength. Figures 5(a)-5(c) show that the dashed line is a linear equation fitting plot at three conditions. The Hall-Petch equation was used with linear fitting to obtain the result in Figure 5(a)
H =5.5 + 64.9D
This equation uses a probable lattice friction stress of 5.5 GPa
and a Hall-Petch constant of 64.9 GPa A for the as-deposited Ta thin films, which is shown in Figure 5(a). The Hall-Petch equation was also used with linear fitting to reach the result in Figure 5(b)
H = 10.2 + 33.5D
This equation uses a probable lattice friction stress of 10.2 GPa and a Hall-Petch constant of 33.5 GPa A for the postannealed 150°C Ta thin films. Moreover, the Hall-Petch equation was also used with linear fitting to reach the result in Figure 5(c)
H =9.9 + 39.7D
This equation uses a probable lattice friction stress of 9.9 GPa and a Hall-Petch constant of 39.7 GPa A for the postannealed 250°C Ta thin films. About the linear fitting discrepancy in Figures 5(b)-5(c), it can be reasonably concluded that the Berkovich indenter of MTS Nanoindenter XP at nanoindention measured process touches some defects or impurity and induces a linear fitting discrepancy. The slope of the Hall-Petch equation at RT is larger than the Hall-Petch equation using postannealing treatments, which indicates that the refined grains at RT sufficiently and efficiently affect the hardness levels. This result is consistent with the "Hall-Petch" effect.
Figures 6(a)-6(b) show the contact angle results of Ta films under three conditions with water and diiodomethane as the test liquids. The contact angles of all films were smaller than 90°, which indicates that the Ta films are hydrophilic. The trend of the contact angle shows that the as-deposited thinner films were smaller than the postannealed thicker films with water as the test liquid. In contrast, the trend of the contact angle shows that the as-deposited thinner films were larger than postannealed thicker films with diiodomethane as the test liquid. Therefore, the various thicknesses, as-deposited condition, and postannealing treatments were sensitive to the contact angle because of crystalline degree of films [22]. The corresponding surface energy of Ta films was obtained by contact angle calculation, as shown in Figure 6(c) [14-16]. This figure shows that the surface energy of as-deposited thinner films was larger than that of postannealed thicker films. It suggests that the weaker crystallization and smaller mean grain size caused a high surface energy and strong adhesion. The surface energy is a crucial index to estimate the adhesion of films. The higher surface energy
i ' i ' i '
Fitting Hall-Petch equation
H = 5.5 + 64.9D_1/2
(Mean grain size) 1/2 (A 1/2)
■ Experimental results ---Fitting line
0.09 0.1 0.11
(Mean grain size)-1/2 (A 1/2)
■ Experimental results ---Fitting line
13.8 13.6 13.4
I 13.2 n
K 13 12.8
(Mean grain size) 1/2 (A 1/2)
■ Experimental results ---Fitting line
Figure 5: Experimental hardness as a function of mean grain size, fitted using the Hall-Petch equation. (a) Was deposited at RT only, (b) postannealed at 150°C for 1 h, and (c) postannealed at 250°C for 1 h.
indicated that the film had a stronger adhesion. Based on this result, the optimal surface energy was 51.56 mJ/mm2 at 500 A of the as-deposited Ta sample, which is suitable for use as a seed layer and buffer layer in MRAM application and semiconductor process.
4. Conclusion
In conclusion, the experiment revealed the nanomechanical and adhesive properties of as-deposited and postannealed Ta thin films of various thicknesses under three conditions. The XRD structure and mean grain size show that strong crystallization and a large mean grain size occurred under the
postannealing condition and thicker thickness. Moreover, the high nanomechanical phenomenon of Ta films was observed at the as-deposited condition and thin thickness, which matched the "Hall-Petch" effect, and was suitable for use in seed layer and capping layer applications because of grain refinement. The highest surface energy and adhesion of Ta films were obtained at 500 A of as-deposited Ta film. Based on the nanomechanical and adhesive properties, the optimal Ta condition was observed at 500 A of the as-deposited Ta film, and the highest H, E, and surface energy were 15.6 GPa, 180 GPa, and 51.56 mJ/mm2, respectively. Therefore, it is suitable for combination with other layers or to protect other films in magnetic field and semiconductor process applications.
"m 68 e
1000 Ta thickness (A)
By test liquid water -■- RT
-•- TA= 150° C -A- TA = 250°C
1000 Ta thickness (A)
By test liquid diiodomethane -■- RT
-•- TA = 150° C -A- TA = 250° C
1000 Ta thickness (A)
TA = 150° C TA = 250° C
Figure 6: Adhesion properties of Ta samples under three conditions. (a) Contact angle with test liquid water, (b) contact angle with test liquid diiodomethane, and (c) surface energy.
Acknowledgment
This work was supported by the National Science Council, under Grant no. NSC100-2112-M214-001-MY3. The author would like to thank for experimental assistance of Professor C. F. Wang.
References
[1] R. Law, R. Sbiaa, T. Liew, and T. C. Chong, "Effects of Ta seed layer and annealing on magnetoresistance in CoFe/Pd-based pseudo-spin-valves with perpendicular anisotropy," Applied Physics Letters, vol. 91, no. 24, Article ID 242504, 3 pages, 2007.
[2] M. Kowalewski, W. H. Butler, N. Moghadam et al., "The effect of Ta on the magnetic thickness of permalloy (Ni81Fe19) films," Journal of Applied Physics, vol. 87, no. 9, pp. 5732-5734, 2000.
[3] W. Peng, O. Keitel, R. H. Victora, E. Koparal, and J. H. Judy, "Co/Pt superlattices with ultra-thin Ta seed layer on NiFe underlayer for double-layer perpendicular magnetic recording media," IEEE Transactions on Magnetics, vol. 36, no. 5 I, pp. 2390-2392, 2000.
[4] K. Weiss, S. Riedel, S. E. Schulz et al., "Development of different copper seed layers with respect to the copper electroplating process," Microelectronic Engineering, vol. 50, no. 1-4, pp. 433440, 2000.
[5] W. P. Jayasekara, S. Zhang, D. Mauri, S. Nguyen, and T. Shatz, "Etching of spin-valve capping layers for sensor stabilization
applications," IEEE Transactions on Magnetics, vol. 39, no. 5, pp. 2381-2383, 2003.
[6] A. G. Roy and D. E. Laughlin, "Effect of seed layers in improving the crystallographic texture of CoCrPt perpendicular recording media," Journal of Applied Physics, vol. 91, no. 10, pp. 8076-8078, 2002.
[7] Y. T. Chen, Y. C. Lin, S. U. Jen, J. Y. Tseng, and Y. D. Yao, "Effect of Ta seed layer on crystalline structure and magnetic properties in an exchange-biased Co/IrMn system," Journal of Alloys and Compounds, vol. 509, no. 18, pp. 5587-5590, 2011.
[8] T. H. Meen, W. R. Chen, C. J. Huang, and C. J. Chiu, "Thin copper seed layers in interconnect metallization using the electroless plating process," Japanese Journal of Applied Physics, vol. 43, no. 8, pp. 5100-5104, 2004.
[9] S. U. Jen, Y. T. Chen, N. T. Yang, and W. C. Cheng, "Mechanical and structural properties of Permalloy films on glass and/or Si(111) substrates," Applied Physics A, vol. 94, no. 2, pp. 431-436, 2008.
[10] S. R. Jian, J. S. C. Jang, Y. S. Lai et al., "Mechanical properties of InGaN thin films deposited by metal-organic chemical vapor deposition," Materials Chemistry and Physics, vol. 109, no. 2-3, pp. 360-364, 2008.
[11] S. R. Jian, I. J. Teng, P. F. Yanget al., "Surface morphological and nanomechanical properties of PLD-derived ZnO thin films," Nanoscale Research Letters, vol. 3, no. 5, pp. 186-193, 2008.
[12] S. R. Jian, J. S. C. Jang, G. J. Chen, H. G. Chen, and Y. T. Chen, "Nanoindentation on a-plane ZnO thin films," Journal of Alloys and Compounds, vol. 479, no. 1-2, pp. 348-351, 2009.
[13] K. M. Yin, L. Chang, F. R. Chen et al., "Oxidation of Ta diffusion barrier layer for Cu metallization in thermal annealing," Thin Solid Films, vol. 388, no. 1-2, pp. 27-33, 2001.
[14] K. Ma, T. S. Chung, and R. J. Good, "Surface energy of thermotropic liquid crystalline polyesters and polyesteramide," Journal ofPolymer Science B, vol. 36, no. 13, pp. 2327-2337,1998.
[15] D. K. Owens and R. C. Wendt, "Estimation of the surface free energy of polymers," Journal of Applied Polymer Science, vol. 13, no. 8, pp. 1741-1747, 1969.
[16] D. H. Kaelble and K. C. Uy, "Reinterpretation of organic liquid-polytetrafluoroethylene surface interactions," Journal of Adhesion, vol. 2, pp. 50-60,1970.
[17] B. D. Cullity, Elements of X-Ray Diffraction, Addison-Wesley, Reading, Mass, USA, 2nd edition, 1978.
[18] Y. T. Chen and C. C. Chang, "Effect of grain size on magnetic and nanomechanical properties of Co60Fe20B20 thin films," Journal of Alloys and Compounds, vol. 498, no. 2, pp. 113-117, 2010.
[19] Y. T. Chen and C. W. Wu, "Effect of grain size on nanoindentation property of Co60Fe20B20 thin film," Journal of Alloys and Compounds, vol. 551, pp. 360-364, 2013.
[20] Y. T. Chen and C. W. Wu, "Effect of grain size on nanomechanical property Ni80Fe20 thin film," Intermatallics, vol. 34, pp. 8993, 2013.
[21] R. Venkatraman and J. C. Bravman, "Separation of film thickness and grain boundary strengthening effects in Al thin films on Si," Journal of Materials Research, vol. 7, no. 8, pp. 2040-2048, 1992.
[22] S. K. Wang, Y. T. Chen, and S. R. Jian, "Determining contact angle and surface energy of Co60Fe20B20 thin films by magnetron sputtering," Journal of Nanomaterials, vol. 2011, Article ID 291935, 4 pages, 2011.
Copyright of Journal of Nanomaterials is the property of Hindawi Publishing Corporation and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use.