Scholarly article on topic 'Tm3+ Modified Optical Temperature Behavior of Transparent Er3+-Doped Hexagonal NaGdF4 Glass Ceramics'

Tm3+ Modified Optical Temperature Behavior of Transparent Er3+-Doped Hexagonal NaGdF4 Glass Ceramics Academic research paper on "Nano-technology"

Share paper
Academic journal
Nanoscale Res Lett
OECD Field of science

Academic research paper on topic "Tm3+ Modified Optical Temperature Behavior of Transparent Er3+-Doped Hexagonal NaGdF4 Glass Ceramics"

E et al. Nanoscale Research Letters (2017) 12:402 DOI 10.1186/s11671-017-2167-9

Nanoscale Research Letters


Tm3+ Modified Optical Temperature Behavior of Transparent Er3+-Doped Hexagonal NaGdF4 Glass Ceramics

Chengqi E1, Yanyan Bu1, Lan Meng1,2 and Xiaohong Yan


Open Access



Er3+-doped and Er3+-Tm3+-co-doped transparent hexagonal NaGdF4 glass ceramics are fabricated via melt-quenching method. The emissions of Er3+-doped NaGdF4 glass ceramics are adjusted from the green to red by varying the concentration of Tm3+ ion under the excitation of 980 nm. The spectrum, thermal quenching ratio, fluorescence intensity ratios, and optical temperature sensitivity of the transparent glass ceramics are observed to be dependent on the pump power. The maximum value of relative sensitivity reaches 0.001 K-1 at 334 K in Er3 +-doped NaGdF4, which shifts toward the lower temperature range by co-doping with Tm3+ ions, and has a maximum value of 0.00081 K-1 at 292 K. This work presents a method to improve the optical temperature behavior of Er3+-doped NaGdF4 glass ceramics. Moreover, the relative sensitivity SR is proved to be dependent on the pump power of 980-nm lasers in Er3+-doped NaGdF4 and Er3+-Tm3+-co-doped NaGdF4.

Keywords: NaGdF4 glass ceramic, Er3+, Tm3+, Excitation power, Sensitivity


The conversion of infrared radiation to visible light has generated much of the attention in up-conversion (UC) processes, particularly in trivalent lanthanide ions (Ln3+)-doped UC materials [1-5], due to wide applications in the visible detection of infrared radiation, solar cells, and optical temperature sensing [6-10]. Among these applications, optical temperature sensors based on the fluorescence intensity ratio (FIR) technique were reported as a good method to measure temperatures in nanoscales [11, 12]. Er3+ has been proved as excellent ions in the field of optical temperature sensors, since it has the two couples of adjacent thermally coupled energy levels (2Hii/2, 4S3/2) and (2D7/2, 4G9/2), whose relative emission intensities are strongly dependent on the temperature [13]. Santos investigated the maximum sensitivity of optical temperature sensing using up-conversion fluorescence emissions was 0.0052/°C in Er3+-Yb3+ co-doped Ga2S3:La2O3 chalcogenide glass [14]. León-Luis

* Correspondence:

1College of Electronic Science and Engineering, Nanjing University of Posts and Telecommunications, Nanjing 210023, China

2Key Laboratory of Radio Frequency and Micro-Nano Electronics of Jiangsu Province Nanjing, Jiangsu 210023, China

Fulllist of author information is available at the end of the article

researched that the temperature sensor had highest sensitivity of 0.0054 K-1 based on the Er + green up-converted emission in a fluorotellurite glass [15]. Du et al. disclosed that the Er3+/Yb3+-co-doped Nao.5Gdo.5MoO4 nanoparti-cles had a maximum sensitivity of 0.00856 K-1 which is independent on the dopant concentration [16]. Zheng et al. observed five-photon up-conversion emissions of Er3 + for optical temperature sensing which had highest sensitivity was 0.0052 K-1 [17]. However, those articles were reported the sensitivity of Er3+-doped optical temperature material which are mainly affected by host matrix and lacked the research of influence on excitation power. In fact, the intensity of the thermally coupled energy level will vary with the intensity of the excitation power. Wang et al. found that the thermal quenching ratio and temperature sensitivity from thermally coupled energy levels of Er3+-doped transparent Sr0.69La0.31F2.31 glass ceramics were dependent on the pump power [18]. Bednarkiewicz's group observed that the highest sensitivity value was dependent on the pump power for LiYb-P4O12:0.1%Er3+ nanocrystals [19]. Similar result has been reported in Er3+-doped Y2SiO5 powders [20]. The optical thermometry at different excitation power was different, since the fluorescence intensity ratios were affected by the

Springer Open

© The Author(s). 2017 Open Access This article is distributed under the terms of the Creative Commons Attribution 4.C International License (, which permits unrestricted use, distribution, anc reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

excitation powers. Thus, it is necessary to explore the optical temperature behavior at the different excitation powers.

Among the reported host materials, NaGdF4 nanocrys-tals have been confirmed as an excellent luminescent host matrix for various optically active Ln + in optical temperature sensor due to their relative low phonon energy and excellent chemical stability [21, 22]. Based on the couple thermally coupled energy levels 2H11/2 and 4S3/2 of Er3+ ion, the optical temperature properties of Er3+-doped NaGdF4 was reported [23]. However, the abovementioned work did not consider influence of excitation power to the optical temperature property of Er3+-doped NaGdF4. The optical temperature property of the Er3+ ions depends on the relative changes in the green emission intensity of thermally coupled energy levels 2H11/2 and 4S3/2 level. The luminescent of Er3+ ions was adjusted by Tm3+ ions through the energy transfer from Er3+ ions to Tm3+ ions [24-28]. Thus, the optical property of Er3+-doped NaGdF4 glass ceramics may be adjusted by the introduction of the Tm3+ ions.

In this paper, Er3+ single-doped and Er3+-Tm3+-co-doped hexagonal NaGdF4 glass ceramics were fabricated to illustrate the abovementioned issues. It is found that the luminescent of Er3+-doped NaGdF4 glass ceramics is tuned from green to red by controlling the concentration of Tm3+ ions. The effects of doping Tm3+ ions on thermal quenching ratio, population mechanism of thermally coupled levels, and temperature sensitivity are also observed by using the different excitation powers. It was observed that the optical temperature sensitivity of Er3 +-doped and Er3+-Tm3+-co-doped NaGdF4 glass ceramics remained substantially increase with the increase of excitation power to the lower temperature field and reached the maximum sensitivity under 322.4 mW/cm2 excitation.


The glass ceramics samples with mole composition of 70.1SiO2-4.3Al2O3-1.8AlF3-2.3Na2CO3-18.5NaF-(2.4-x)Gd2O3-0.6Er2O3-xTm2O3 (x = 0, 0.05, 0.1, 0.15, 0.2) were prepared by melt-quenching method, which were labeled as the NGF1, NGF2, NGF3, NGF4, and NGF5, respectively. High pure reagents of SiO2, Al2O3, AlF3, Na2CO3, NaF, Gd2O3, Er2O3, and Tm2O3 were used as raw materials. Accurately weighed 20 g batches of raw materials were ground in a mortar with fully mixed and then melted in a covered corundum crucible at 1600 °C for 45 min. The melts were cast quickly into a brass mold plates and pressed it. The obtained glass ceramics were annealed at 700 °C for 20 h to form transparent ceramics through a crystallization process in the annealing furnace. All samples were polished optically for further characterization. For a better comparison of the

role of Tm3+ ions, the NGF1 and NGF3 are used for mainly contrast sample.

Structures of the samples were investigated by X-ray diffraction (XRD) using XTRA (Switzerland ARL) equipment provided with Cu tube with Ka radiation at 1.54056 nm. The shape and size of the samples were observed by a transmission electron microscope (JEOL JEM-2100). Luminescence spectra were obtained by an Acton SpectraPro SP-2300 Spectrophotometer with a photomultiplier tube equipped with the xenon lamp as the excitation sources. Different temperature spectra were obtained using an INSTEC HCS302 Hot and Cold System.

Results and Discussion

The structural properties of Er3+-Tm3+ -co-doped transparent NaGdF4 glass ceramics are studied by the transmission electron microscope (TEM), the highresolution transmission electron microscope (HRTEM) images, and XRD, as shown in Fig. 1. It could be found that the dark spherical or irregular block nanocrystals were lying on the gray background and the size of NaGdF4 crystallite is about 30-55 nm, as shown in Fig. 1a. In Fig. 1b, the HRTEM image shows lattice fringes with an observed interplanar distance is about 0.23 nm, it can be attributed to the (111) crystal plane of NaGdF4 crystals. As shown in Fig. 1c, the position and intensity of all diffraction peaks could be readily assigned as hexagonal phase NaGdF4 based on the standard XRD pattern (JCPDS 27-0667), which indicates that the hexagonal phase NaGdF4 with a crystalline nature can be readily prepared by melt-quenching method.

The absorption spectra of NGF1 and NGF3 from 320 to 1600 nm are shown in Fig. 2. It corresponds to the transition from the ground state (except for 450 nm absorption) to the high energy level are marked in the figure. The absorption peaks of 378, 405, 488, 520, 652, 972, and 1532 nm are assigned to the transitions of Er3+ ions from ground state 4I15/2 to the excited state 4G11/2, 2H9/2, 4F7/2, 2Hh/2, 4F9/2, 4Ih/2, and 4Ii3/2, respectively. The absorption peak of Tm3+ ions have 450 and 1206 nm, which corresponds of energy transfer is D2^ 3F4 and 3H5 ^ H6. It is noteworthy that the shape change of peak at 800 nm absorbs wavelengths after doping Tm3+ ions; it may be absorbed by Er3+ ions and Tm3+ ions together. The absorption around 800 nm in the co-doped samples may be originating from the transitions Er3+:4I15/2^4I9/2 and Tm3+:3H6^3H4, respectively.

The room temperature up-converted luminescence spectra of samples NGF1, NGF2, NGF3, NGF4, and NGF5 are investigated under the excitation of a 980-nm laser diode. The characteristic emissions of Er3+ ions ranging from 300 to 900 nm can be clearly observed in Fig. 3a. Emission bands located at 509 nm (NGF1),

30 40 50


Fig. 1 (a) TEM and (b) HRTEM micrograph images of NGF3. c XRD pattern of the NGF3 (JCPDS 27-0699)

542 nm (green, NGF3), and 660 nm (red, NGF3) are assigned to 2H9/2^%5/2, 4S3/2^%5/2, and 4F9/2^4Ix5/2 transitions of Er3+, respectively. As shown in Fig. 3a, with the addition of Tm3+ ions and the concentration increases, the 509 nm emission disappear, the 542 nm wavelength intensity decreases first and then the change is not obvious; at meanwhile, the 660 nm wavelength increases first and then decreases. In order to clearly show the relative changes between 542 nm wavelength and 600 nm wavelength intensity, the red to green intensity ratio shows in Fig. 3b. The red to green intensity ratio is

Er3+:4Gll /378nm

Er3+:2Hn;2 520nm



Er :4I , +Tm3

3H. Tm^H


Er : I,.

11/2 972nm

9/2 488nm Er3+:4F,


500 1000


Fig. 2 The absorption spectra of NGF1 and NGF3

increased first and then maintain a certain range of ups and downs with the Tm3+ ions concentration increased. In combination with Fig. 3a, b, the luminescence intensity of different wavelength has changed with the Tm3+ ions doping, while the position of the peak is unchanged. Therefore, Tm3+ ions have the effect of modified luminescence in Er3+-doped NaGdF4 glass ceramics.

In order to analyzing the Tm3+ modified luminescence, the energy level diagram and the photoluminescence mechanism are illustrated in Fig. 4. In Er3+ single-doped NaGdF4, the 509 nm, 542 nm (green), and 660 nm (red) emission bands are observed through the transitions from 2H9/2, 4S3/2 and 4F9/2 states to 4Ii5/2 state, respectively. By co-doping Er3+ and Tm3+ ions in NaGdF4, under the 980 nm excitation, the absorption of 980 nm photons results in direct excitation of Er3+ ions from the ground 4I15/2 state to the excited station I11/2 state through a ground-state absorption (GSA) process. Then, Er3+ ions in the 4I11/2 state are promoted to the higher station 4F7/2 state through an excited-state absorption (ESA). After a series of nonradioactive relaxation (NR) from 4I7/2, the 542 nm (green), 660 nm (red) emission bands are observed through the transitions from 4S3/2 and 4F9/2 states to 4I15/2 state, respectively. And the green emission is reduced by an energy transfer (ET) from Er3+ to Tm3+ (5, Fig. 4): Er3+ (4S3/2)+Tm3+ (3H6)^Er3+ (4I9/2)+Tm3+ (3F4) [29]. In contrast, the population of 4F9/2 level is based on the ET processes as follows (6, Fig. 4): Er3+ (4In/2)+Tm3+ (3F4)^Er3+ (%

Wavelength (nm) Tm3+(mol%)

Fig. 3 (a) The luminescence spectra and (b) red to green intensity ratio of 1%Er3+,x%Tm3+-co-CopeC NaGdF4 (x = 0, 0.05, 0.1, 0.15, 0.2)

2)+Tm3+ (3H6), which had already been confirmed [25, 30]. There are two important energy levels of 660 nm emission enhancement, Er3+ (4I11/2) and Tm3+ (3F4); the population of Er3+ (4I11/2) is through NR process from Er3 + (4I9/2); however, we found that Tm3+ (3F4) populated may be via three kinds of ET: the first (ET1, Fig. 4) is Er3+ (4I13/J)^Tm3+ (3F4); the second (ET2, Fig. 4) is Er3+ (In/ 2)^Tm3+ (3H5) with subsequent NR from 3H5 (Tm3+) to 3F4 (Tm3+); and the third is previously mentioned energy transfer of green emission depopulation: Er3+ (4S3/2)+Tm3 + (3H6)—Er3+ (4I9/2)+Tm3+ (3F4). Combined with Figs. 3a and 4, the green emission drastically reduced with the Tm3+ ions doped; the ET of Er3+ (4S3/2)+Tm3+ (3H6)—Er3 + (4I9/2)+Tm3+ (3F4) may dominate the population of Tm3 + (3F4). And the red emission is quenched at the large Tm3+ concentration. It can be ascribed to the ET(ET3, Fig. 4): 4F9/2 (Er3+)—3F2(Tm3+).30 Combined with the above analysis, we can divide the energy transfer of Er3 +-Tm3+ luminescence systems into two parts: (a) the excited state 4I11/2 state from the ground-state absorption

and then through an excited-state absorption to the higher station 4F7/2 state by Er3+, through finally nonradiative relaxation from 4I7/2, the 542 nm (green), 660 nm (red) emission bands are observed; (b) the population of red-emitting and the depopulation of green-emitting can be attributed to an energy loop, Er3+ (4S3/2) —Er3+ (4I9/2) —Er3+ (4I11/2) ^Tm3+ (3F4) —Er3+ (4F9/2), which implements the modified luminescence of Tm3+ ions.

The temperature sensing properties based on the luminescence emissions at 509, 529, 542, 660, and 805 nm of Er3+ single-doped (NGF1) and the luminescence emissions at 529, 542, and 660 nm of Er3+-Tm3+-co-doped NaGdF4 glass ceramics (NGF3) have been shown in Fig. 5, with the temperature ranging from 298 to 573 K, respectively. The two green up-conversion emissions bands at about 529 and 542 nm correspond to the 2H11/2—4I15/2 and 4S3/2—*4I15/2 transitions of Er3+, respectively. The 509, 660, and 805 nm emissions correspond to the 2H9/2—4I15/ 2, 4F9/2—4I15/2 and 4I9/2—4I15/2 transitions of Er3+, respectively. With the increased of the temperature, it can be found that the emission intensities of 4S3/2 level decrease markedly. The 2H11/2 level may be also populated from the 4S3/2 level by thermal excitation, due to the thermal population and depopulation at high temperature [31]. The relative population of the "thermally coupled" 2H11/2 and 4S3/2 levels follows a Boltzmann-type population distribution, which has already been confirmed [32, 33], leading to variation in the transitions of 2H11/2—4I15/2 and 4S3/ 2—4I15/2 of Er3+ at the elevated temperature.

The thermal quenching ratio (Rq) is a key parameter to evaluate the affection of temperature on luminescence quenching [16]. The Rq of emission band with temperature change is defined as follow:

Rq = 1-t (!)

Here, IT is luminescence intensity at different temperature T, and I0 is luminescence intensity at room



373 ' 423 ^

473 523 573

Wavelength(nm) Wavelength(nm)

Fig. 5 UC emission spectra of (a) NGF1 and (b) NGF3 in the wavelength range of 200-900 nm at various temperatures

temperature. The values of Rq for the 409, 529, 542, 660, and 805 nm emissions of NGF1 and NGF3 show in Fig. 6 with 66.8 and 322.4 mW/cm2 excitation power. In Fig. 6a, with the temperature increase, the value of Rq in 529 nm grows slowly than the value in 542 nm, which means emission intensity of 529 nm reduce slowly than emission intensity of 529 nm. In Fig. 6b, it shows a different trend with the increase of temperature. The value of Rq at 542 nm emission band increases with temperature increase. Oppositely, the value of Rq of the 529 nm emission band shows some negative values and decreases firstly and then increases with increasing temperature, which means that the 2H11/2 state is populated thermally at high temperature [34]. In Fig. 6a, the values of Rq for the 409 nm emissions increase with temperature increase quickly. Compared with Fig. 6a, b at 660 nm, we could obverse that with the addition of Tm3+ ions, Rq become a relatively large positive value, which means Er3+-Tm3+ -co-doped NaGdF4 at 660 nm luminescence with temperature was changed significantly. The

intensity of 800 nm emissions can be enhanced a lot by the increase of temperature and the decrease of excitation power in Fig. 6a, but it does not appear in Er3+-Tm3+-co-doped NaGdF4.

To explore the origin of green emission and red emission of Er3+ ions at high temperatures, the relation between UC emission intensity I and laser light intensity P is expressed as:

I«Pn (2)

where I is the emission intensity, P is incident pump power, and n is the number of pump photons absorbed in the up-conversion process [35]. Figure 7 shows loglog plots of up-conversion intensity and pumping power for green and red at the different temperatures in NGF3. The slopes of fitted lines for 542 and 660 nm emissions change little at two temperature points of 298 and 573 K, and all values of n are less than 2 but greater than 1, indicating that 524 and 660 nm emissions come

450 500 550 600 300 350 400 450

T (K) T (K)

Fig. 6 Thermalquenching ratios (RQ) of (a) NGF1, (b) NGF3 at low 66.8 mW/cm2 excitation power and at high 322.4 mW/cm2 excitation power

542 nm emission

slope n=1.87

slope n=1.97

■ 298K • 573K

660 nm emission

s slop=1.95

s slop=1.99

298K 573K

1.8 1.9 2.0 2.1 2.2 2.3 2.4 2.5 2.6 1.8 1.9 2.0 2.1 2.2 2.3 2.4 2.5 2.6

Log P(mw/mm )

Log P(mw/mm )

Fig. 7 Log-log plots of intensity and pumping power for (a) 542 nm, (b) 660 nm emissions at 298 and 573 K in NGF3

from two-photon up-conversion process regardless of the high temperature or low temperature.

In summary, two adjacent energy levels, the upper 2H11/2 level and the lower 4S3/2, can relatively change with temperature increase, which is fitting the Boltzmann distributing law, and it may be used to be as thermally coupled levels [36]. According to the theory in [16] and [23], the population ratio of 2H11/2 to 4S3/2 from thermally coupled levels of Er3+ is defined as:

iu -¿e. / n

R = — = AeKBT (3)

where A is a fitting constant that depends on the experimental system and intrinsic spectroscopic parameters; △E is the fitting energy difference between thermally coupled levels; KB is the Boltzmann constant; T is the absolute temperature. The luminescence intensity ratio between Iu and IL will change regularly with the temperature increase. A function relation between the luminescence intensity ratio and temperature can be

determined through fitting some data points at different temperatures. The temperature-dependent fluorescence intensity ratios between the 2H11/2 and 4S3/2 of Er3+ in NGF1 and NGF3 samples from 298 to 573 K are shown in Fig. 8 under different excitation power. The experimental data are fitted by Eq. (3). It can be observed that the fittings agree well with the experimental data. The curve value of R is dependent on excitation power whether NGF1 or NGF3. It means that the fluorescence intensity ratios of the coupled levels of 2H11/2 and 4S3/2 susceptible to the pumping power in Er3+ single-doped and Er3+-Tm3+-co-doped NaGdF4 glass ceramics. Comparing Fig. 8b with Fig. 8a, under the same excitation power, it can be seen that the curve matching formula is not the same, suggesting that the population ratio of 2H11/2 to 4S3/2 was changed after doped Tm3+ ions.

It is important to investigate the sensing sensitivity for further understand the temperature response of NGF1 and NGF3. The sensitivity of optical thermometry is the rate of change of R in response to the variation of temperature [37, 38]. The relative

R=1.24689*exp(-376.06533/T) R=1.27672*exp(-701.27372/T) R=1.31998*exp(-733.8I

1.36018*exp(-761.11858/T) !=1.39094*exp(-784.97598/T)

R=0.92053*exp(-615.38621/T) R=0.93628*exp(-636.82575/T) \ 1 -66.8mW/ciTf -^S^W/CIT — 142.4mW/cm2 -184ITW/CT — 248.8mW/cm2 -322.4ITW/CIT


//¡fit R=0.98576*exp(- 688.34057/T)

\ R=1.02144*exp(-712.51774/T)

- >R=1.06652*exp(-737.30979/T)

300 350 400 450 500 550 600 650 700 Temperature(K)

Fig. 8 Excitation power-dependent emission intensity ratio glass ceramics of 2H11/2/4S3/2 on (a) NGF1 and (b) NGF3

300 350 400 450 500 550 600 650 700 Temperature(K)





sensitivity SR and the absolute sensitivity SA are defined as:

Sr = -T= = R-2


1 dR AE

RdT K BT 2

where the AE is the energy difference between thermally coupled levels, KB is the Boltzmann constant, T is the absolute temperature, and R is the luminescence ratio between the two thermally coupled levels [39]. Figure 9 depicts the curves of SR of NGF1 and NGF3 samples dependent on temperature under different excitation power. Two samples show the high sensitivity at low excitation. The maximum SR value of Er3+-doped NaGdF4 is estimated to be 0.001 K-1 at 334 K, while Er3 +-Tm3+-co-doped NaGdF4 has the maximum SR value that is 0.00081 K-1 at 292 K. Moreover, it is worth noting that the sensitivity peak shifts toward the lower temperature range after doping with Tm3+ ions.

From Fig. 9, the slopes of fitted lines for NGF1 and NGF3 are increased first and then slowly decrease with the increase of the temperature range from 0 to 2000 K, revealing that NGF1 and NGF3 can monitor a wide range of temperature. It can be clearly seen that with the addition of Tm3+ ions, the maximum sensitivity and the maximum sensitivity temperature are changed. Compared to NGF1 which has maximum sensitivity in temperature is about 334 K, NGF3 has maximum sensitivity in the lower temperature than in NGF1 that is about 292 K. It means Tm3+ ions can change the sensitivity and temperature measurement range. And it is very sensitive to measure temperature from 334 to 405 K by using the fluorescence intensity ratio of the NGF1 under excitation power from 322.4 to 66.8 mW/

cm2. This means that Er3+-doped NaGdF4 can be used So, it further explains that Er3+-co-doped NaGdF4

temperature of about 292 K. It is well known that most of the up-conversion rare earth ion-doped optical temperature materials exhibit superior sensitivity at moderate to high temperatures [40-42]. There are very few reports of optical thermometry around room temperature. Thus, NGF3 is suitable for monitoring the temperature around 20 °C. One can find that the values of SR decrease with increase excitation powers basically in NGF1, but it first decrease and then increase with increase excitation powers in NGF3. The largest SR appears when the excitation power is 322.4 mW/cm2. In addition, it can be observed that the temperature of the location about the maximum sensitivity is close to the lower temperature range as the excitation power increases. Thus, a general rule can be obtained in NGF1 and NGF3, which are more sensitive for temperature measurement in lower temperature environments as the excitation power increases. The NGF1 not only has maximum of SR larger than NGF3 but also has the value of SR that is more and corresponds to ordinary rules with the increase of excitation power than NGF3. Thus, the Er3+-doped NaGdF4 is a better candidate for optical temperature sensors than Er3+-Tm3+-co-doped NaGdF4 by considering the stabilities induced by temperature and excitation powers. According to Eq. (4), the sensitivity is determined by the energy difference (AE) between thermally coupled levels. Thus, the energy difference (AE) in NGF1 and NGF3 glass ceramics is greater than some other RE (rare earth ion)-doped materials, which leads to the higher sensitivity of NGF1 and NGF3 glass ceramics. In order to compare the sensitivity with various rare ions for optical thermometry, some of the reports of sensitivities of various rare earth ions are presented in Table 1. It shows that the sensitivity of Er3+-doped NaGdF4 glass ceramics is well than some other rare earth ion-doped material.

for intermediate temperature measurements. As can be seen from Fig. 9b, NGF3 has a high sensitivity at a low

glass ceramic will be a good candidate for highperformance optical thermometry.

Tempurature(K) Tempurature(K)

Fig. 9 Excitation power-dependent relative sensitivity SR of (a) NGF1 and (b) NGF3

Table 1 Values of sensitivity for various rare earths are presented, and the involved transitions from thermally coupled levels as well as temperature range are included

Rare earth ions Host Transitions Temperature range (K) Sa Ref.

Er3+ NaGdF4 2H11/2,4S3/2—^4|15/2 298-593 806/T2 This work

Er3+,Tm3+ NaGdF4 2H11/2,4S3/2—^4|15/2 298-593 737/T2 This work

Tm3+,Yb3+ NaNbC>3 1G4,3F2,3,3H4—3H6 293-353 93.53/T2 [43]

Tm3+,Yb3+ Y2O3 1D2—3F4,3H4—3H6 10-300 566.91/T2 [44]

Ho3+ In-Zn-Sr-Ba 5F4/5S2—5Vl7 20-300 181.64/T2 [45]

Ho3+ TeO2 5F4/5S2—5l8 265-440 255/T2 [46]


In summary, Er3+-doped NaGdF4 and Er3+-Tm3+-co-doped NaGdF4 glass ceramics were prepared by a melt-quenching method and subsequent heating. The samples were investigated through XRD, TEM, and luminescence spectra measurement. Under laser excitation of 980 nm, these glasses strongly emitted light in the visible region, ranging from green to red. A visible emission which can be tuned from the green to the red color by varying the Tm3+ ion concentration is achieved under the 980 nm excitation. Meanwhile, the emission intensities of the Er3 +-doped and Er3+-Tm3+-co-doped transparent NaGdF4 glass ceramics were found to be temperature dependent. It was found that the spectrum structure, thermal quenching ratio, fluorescence intensity ratio, and sensitivity from thermally coupled levels were strongly dependent on the change of pump powers. Optical temperature sensing of the Er3+-doped and Er3+-Tm3 +-co-doped NaGdF4 transparent glass ceramics in the temperature that ranges from 298 to 573 K is studied. The maximum value of relative sensitivity (SR) is 0.001 K -1 at 334 K under 322.4 mW/mm2 excitation. And it shifts toward the lower temperature range and has a maximum value of 0.00081 K-1 at 292 K after doped with Tm3+ ions. The results indicate that the Er3+-doped and Er3+-Tm3+-co-doped NaGdF4 transparent glass ceramics may be good candidates for the temperature sensor.


△E: Energy difference; ESA: Excited-state absorption; ET: Energy transfer; FIR: Fluorescence intensity ratio; GSA: Ground-state absorption; HRTEM: Highresolution transmission electron microscope; Ln3+: Trivalent lanthanide ions; NGF1: 0.6%Er3+-doped NaGdF4 glass ceramics; NGF2: 0.6%Er3+-0.05%Tm3+ co-doped NaGdF4 glass ceramics; NGF3: 0.6%Er3+-0.1%Tm3+ co-doped NaGdF4 glass ceramics; NGF4: 0.6%Er3+-0.15%Tm3+ co-doped NaGdF4 glass ceramics; NGF5: 0.6%Er3+-0.2%Tm3+ co-doped NaGdF4 glass ceramics; NR: Nonradioactive relaxation; RE: Rare earth ion; RQ: Thermal quenching ratio; SA: Absolute sensitivity; SR: Relative sensitivity; TEM: Transmission electron microscope; UC: Up-conversion; XRD: X-ray diffraction


This work was supported by the National Natural Science Foundation of China (51651202, 11374162, 11504180) and the Scientific Research Foundation of Nanjing University of Posts and Telecommunications (NY215174).

Authors' contributions

CE and XY designed the experiments. CE carried out the synthesis and characterization of the samples, analyzed the results, and wrote the first draft of the manuscript. CE and XY participated in the analyses of the results and discussion of this study. LM, YB, and XY revised the manuscript and corrected the English. All authors read and approved the final manuscript.

Competing interests

The authors declare that they have no competing interests.

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Author details

1College of Electronic Science and Engineering, Nanjing University of Posts and Telecommunications, Nanjing 210023, China. 2Key Laboratory of Radio Frequency and Micro-Nano Electronics of Jiangsu Province Nanjing, Jiangsu 210023, China. 3College of Science, Nanjing University of Aeronautics and Astronautics, Nanjing 210023, China. 4School of Material Science and Engineering, Jiangsu University, Zhenjiang 212013, China.

Received: 13 April 2017 Accepted: 26 May 2017 Published online: 12 June 2017


1. Secu M, Secu CE (2015) Up-conversion luminescence of Er3+/Yb3+ co-doped LiYF4 nanocrystals in sol-gel derived oxyfluoride glass-ceramics. J Non-Cryst Solids 426:78

2. Pablos-Martín AD, Méndez-Ramos J, del-Castillo J, Durán A, Rodríguez VD, Pascual MJ, Pascual M (2015) Crystallization and up-conversion luminescence properties of Er3+/Yb3+-doped NaYF4-based nano-glass-ceramics. J Eur Ceram Soc 35:1831-1840

3. Wang X, Xu T, Cai P, Vu T, Seo H (2017) Controlled synthesis, multicolor luminescence, and optical thermometer of bifunctional NaYbF4:Nd3 +@NaYF4:Yb3+ active-core/active-shell colloidal nanoparticles. J Alloys Compd 691:530-536

4. Babu P, Martín IR, Krishnaiah KV, Seo HJ, Venkatramu V, Jayasankar CK, Lavín V (2014) Photon avalanche upconversion in Ho3+-Yb3+ co-doped transparent oxyfluoride glass-ceramics. Chem Phys Lett 600:34-37

5. Yang K, Cheng G, Liang H (2002) Preparation and spectral analysis of codoped Yb3+/Ho3+ upconversion luminescence glass ceramics. Proc SPIE Vol 4918:405-408

6. Ma L, Bienfang JC, Slattery O, Tang X (2011) Up-conversion single-photon detector using multi-wavelength sampling techniques. Opt Express 19: 5470-5479

7. Mahata M, Kumara KK, Raia VK (2015) Er3+-Yb3+ doped vanadate nanocrystals: a highly sensitive thermographic phosphor and its optical nanoheater behavior. Sens Actuators, B 209:775-780

8. Du P, Yu JS (2015) Effect of molybdenum on upconversion emission and temperature sensing properties in Na0.5 Bi0.5 TiO3: Er/Yb ceramics. Ceram Int 41:6710-6714

9. Du P, Luo L, Li W, Yue Q (2014) Upconversion emission in Er-doped and Er/ Yb-codoped ferroelectric Na0.5Bi0.5TiO3 and its temperature sensing application. J Appl Phys 116:014102

10. Xu W, Zhang Z, Cao W (2012) Excellent optical thermometry based on short-wavelength upconversion emissions in Er3+/Yb3+ codoped CaWO4. Opt Lett 37:4865-4867

11. Fischer LH, Harms GS, Wolfbeis OS (2011) Upconverting nanoparticles for nanoscale thermometry. Chem Int Ed 50:4546-4551 Shinn MD, Sibley WA, Drexhage MG, Brown RN (1998) Optical transitions of

Er + ions in fluorozirconate glass. Phys Rev B Condens Matter 27:6635 Wang X, Liu Q, Bu Y, Liu C, Liu T, Yan X (2015) Optical temperature sensing of rare-earth ion doped phosphors. RSC Adv 5:86219-86236 dos Santos PV, de Araujo MT, Gouveia-Neto AS, Medeiros Neto JA, Sombra ASB (1998) Optical temperature sensing using upconversion fluorescence emission in Er3+/Yb3+-codoped chalcogenide glass. Appl Phys Lett 73:578580

León-Luis SF, Rodríguez-Mendoza UR, Lalla E, Lavín V (2011) Temperature sensor based on the Er3+ green upconverted emission in a fluorotellurite glass. Sens Actuators B 158:208-213

Du P, Luo L, Park H, Yu JS (2016) Citric-assisted sol-gel based Er3+/Yb3 +-codoped b Na05Gd05MoO4: a novel highly-efficient infrared-to-visible upconversion material for optical temperature sensors and optical heaters. Chem Eng J 306:840-848

Zheng K, Song W, He G, Yuan Z, Qin W (2015) Five-photon UV upconversion

emissions of Er3+ for temperature sensing. Opt Express 23:7653-7658

Wang X, Liu Q, Cai P, Wang J, Qin L, Vu T, Seo H (2016) Excitation powder

dependent optical temperature behavior of Er3+ doped transparent Sr0.

69Laa31F2.31 glass ceramics. Opt Express 24:17792-17804

Marciniak L, Waszniewska K, Bednarkiewicz A, Hreniak D, Strek W (2016)

Sensitivity of a nanocrystalline luminescent thermometer in high and low

excitation density regimes. J Phys Chem C 120:8877-8882

Rakov N, Maciel GS (2012) Three-photon upconversion and optical

thermometry characterization of Er3+:Yb3+ co-doped yttrium silicate

powders. Sens Actuators B 164:96-100

Liu CH, Wang H, Zhang XR, Chen DP (2009) Morphology-and phase-controlled synthesis of monodisperse lanthanide-doped NaGdF4 nanocrystals with multicolor photoluminescence. J Mater Chem 19:489-496 Boyer JC, Gagnon J, Cuccia LA, Capobianco JA (2007) Synthesis, characterization, and spectroscopy of NaGdF4: Ce3+, Tb3+/NaYF4 core/shell nanoparticles. Chem Mater 19:3358-336

Chen D, Wan Z, Yan Z (2015) Bulk glass ceramics containing Yb3+/Er3+: ß-NaGdF4 nanocrystals: phase-separation-controlled crystallization, optical spectroscopy and upconverted temperature sensing behavior. J Alloys Compd 638:21 -28

Ledemi Y, Trudel AA, Rivera VAG, Messaddeq Y. Up-conversion emission tuning in triply-doped Yb3+/Tm3+/Er3+ novel fluoro-phosphate glass and glass-ceramics. International Society for Optics and Photonics. 2014; 8982: 89820V

Zou X, Shikida A, Yanagita H, Toratani H (1995) Mechanisms of upconversion fluorescences in Er3+, Tm3+ codoped fluorozircoaluminate glasses. J Non-Cryst Solids 181:100-109

Chai G, Dong G, Qiu J, Zhang Q, Yang Z (2012) 2.7 |im emission from transparent Er3+, Tm3+ codoped yttrium aluminum Garnet (Y3Al5O12) nanocrystals-tellurate glass composites by novel comelting technology. J Phys Chem C 116:19941-19950

Herrmann A, Tylkowski M, Bocker C, Rüssel C (2013) Preparation and

luminescence properties of glass-ceramics containing Sm3+-doped

hexagonal NaGdF4 crystals. J Mater Sci 48:6262-6268

Herrmann A, Tylkowski M, Bocker C, Rüssel C (2013) Cubic and hexagonal

NaGdF4 crystals precipitated from an aluminosilicate glass: preparation and

luminescence properties. Chem Mater 25:2878-2884

Chan EM, Gargas DJ, Schuck PJ, Milliron DJ (2012) Concentrating and

recycling energy in lanthanide codopants for efficient and spectrally pure

emission: the case of NaYF4: Er3+/Tm3+ upconverting nanocrystals. J Phys

Chem B 116:10561-10570

Shen X, Nie Q, Xu T, Peng T, Gao Y (2004) Green and red upconversion emission and energy-transfer between Er3+ and Tm3+ ions in tellurite glasses. Phys Lett A 332:101-106

Quintanilla M, Cantelar E, Cussó F, Villegas M, Caballero AC (2011) Temperature sensing with up-converting submicron-sized LiNbO3:Er3+/Yb3+ particles. Appl Phys Express 4:022601

Wade SA, Collins SF, Baxter GW (2003) Fluorescence intensity ratio technique for optical fiber point temperature sensing. J Appl Phys 94:4743-4756

33. Li C, Dong B, Ming C, Lei M (2007) Application to temperature sensor based on green up-conversion of Er3+ doped silicate glass. Sensors 7:2652-2659

34. Zhou S, Deng K, Wei X, Jiang G, Duan C, Chen Y, Yin M (2013) Upconversion luminescence of NaYF4: Yb3+, Er3+ for temperature sensing. Opt Commun 291:138-142

35. Auzel F (2004) Upconversion and anti-stokes processes with f and d ions in solids. Chem Rev 104:139-174

36. Suyver JF, Aebischer A, García-Revilla S, Gerner P, Güdel HU (2005) Anomalous power dependence of sensitized upconversion luminescence. Phys Rev B Condens Matter 71:125123

37. Dong B, Cao B, Feng Z, Wang W, He Y (2012) Optical temperature sensing through extraordinary enhancement of green up-conversion emissions for Er-Yb-Mo:Al2O3. Sens Actuators B 165:34-37

38. Singh SK, Kumar K, Rai SB (2009) Er3+/Yb3+ codoped Gd2O3 nano-phosphor for optical thermometry. Sens Actuators, A 149:16-20

39. Strek W, Sokolnicki J, Legendziewicz J, Maruszewski K, Reisfeld R, Pavich T (1999) Optical properties of Eu(III) chelates trapped in silica gel glasses. Opt Mater 13:41 -48

40. Leon-Luis SF, Rodríguez-Mendoza UR, Haro-González P, Martín IR, Lavín V (2012) Role of the host matrix on the thermal sensitivity of Er3+ luminescence in optical temperature sensors. Sens Actuators, B 174:176-186

41. Leon-Luis SF, Rodríguez-Mendoza UR, Martín IR, Lalla E, Lavín V (2013) Effects of Er3+ concentration on thermal sensitivity in optical temperature fluorotellurite glass sensors. Sens Actuators, B 176:1167-1175

42. Vetrone F, Naccache R, Zamarrón A, Juarranz de la Fuente A, Sanz-Rodríguez F, Martinez Maestro L, Martín Rodriguez E, Jaque D, García SJ, Capobianco JA (2010) Temperature sensing using fluorescent nanothermometers. ACS nano 4:3254-3258

43. Pereira AF, Kumar KU, Silva WF, Santos WQ, Jaque D, Jacinto C (2015) Yb3 +/Tm3+ co-doped NaNbO3 nanocrystals as three-photon-excited luminescent nanothermometers. Sens Actuators, B 213:65-71

44. Lojpur V, Nikolic M, Mancic L, Milosevic O, Dramicanin MD (2013) Y2O3: Yb, Tm and Y2O3: Yb, Ho powders for low-temperature thermometry based on up-conversion fluorescence. Ceram Int 39:1129-1134

45. González PH, Luis SFL, Pérez SG, Martín IR (2011) Analysis of Er3+ and Ho3+ codoped fluoroindate glasses as wide range temperature sensor. Mater Res Bull 46:1051-1054

46. Singh AK (2007) Ho3+:TeO2 glass, a probe for temperature measurements. Sen and Act A 136:173-177

Submit your manuscript to a SpringerOpen journal and benefit from:

► Convenient online submission

► Rigorous peer review

► Open access: articles freely available online

► High visibility within the field

► Retaining the copyright to your article

Submit your next manuscript at ►